BoneCom® Low-loss, high-strength single-mode fiber SL-G.652.D
Product Performance
Ultra-low transmission loss, @1550nm≤ 0.180dB/km, @1310nm≤ 0.320dB/km.
Optimized PMD characteristics, low splice loss and excellent compatibility.
Optional high screening strength to suit submarine cable requirements.
Application Scenarios
100G and B100G high-speed long-distance transmission systems.
High-capacity ocean communication networks and submarine observation networks.
Broadband metropolitan area network.
Product Specification
|
Characteristics |
Conditions |
Units |
Specified values |
|
Optical Characteristics |
|||
|
Attenuation |
1310nm |
dB/km |
≤ 0.320 |
|
1383nm |
dB/km |
≤ 0.320 |
|
|
1550nm |
dB/km |
≤ 0.180 |
|
|
1625nm |
dB/km |
≤ 0.220 |
|
|
Relative wavelength attenuation changes |
1310nm VS. 1285-1330mn |
dB/km |
≤ 0.04 |
|
1550nm VS. 1525-1575mn |
dB/km |
≤ 0.03 |
|
|
Zero Dispersion Wavelength(λ0) |
- |
nm |
1300-1324 |
|
Zero Dispersion Slope |
- |
ps/nm2·km |
0.073-0.092 |
|
Dispersion |
1550nm |
ps/nm·km |
13.3-18.6 |
|
1625nm |
ps/nm·km |
17.2-23.7 |
|
|
PMD |
- |
ps/√km |
≤ 0.08 |
|
Cable Cutoff Wavelength(λcc) |
- |
nm |
≤ 1260 |
|
Mode Field Diameter (MFD) |
1310nm |
μm |
9.2±0.4 |
|
1550mn |
μm |
10.4±0.5 |
|
|
Attenuation discontinuity |
1310nm |
dB |
≤ 0.03 |
|
1550mn |
dB |
≤ 0.03 |
|
|
Attenuation of the two-way end difference |
1310nm |
dB/km |
≤ 0.03 |
|
1550nm |
dB/km |
≤ 0.03 |
|
|
Geometrical Characteristics |
|||
|
Cladding Diameter |
μm |
125±0.7 |
|
|
Cladding Non-Circularity |
% |
≤ 1.0 |
|
|
Core-Cladding Concentricity Error |
μm |
≤ 0.6 |
|
|
Coating Diameter |
μm |
242±7 |
|
|
Coating-Cladding Concentricity Error |
μm |
≤ 12 |
|
|
Curl (Radius) |
m |
≥ 4 |
|
|
Environmental Characteristics 1550nm &1625nm |
|||
|
Temperature Dependence Induced Attenuation |
-60℃ to +85℃ |
dB/km |
≤ 0.03 |
|
Damp Heat Dependence Induced Attenuation |
85℃ and 85% RH, for 30 days |
dB/km |
≤ 0.03 |
|
Watersoak Dependence Induced Attenuation |
23℃, for 30 days |
dB/km |
≤ 0.03 |
|
Dry Heat Induced Attenuation |
85℃, for 30 days |
dB/km |
≤ 0.03 |
|
Mechanical properties |
|||
|
Tension screening * |
- |
GPa |
0.69 |
|
- |
kpsi |
100 |
|
|
Coating Strip Force |
peak force |
N |
1.3-8.9 |
|
typical average force |
N |
1.0-5.0 |
|
|
Tensile Strength |
Weber Probability 50% |
GPa |
≥ 4.00 |
|
Weber Probability 15% |
GPa |
≥ 3.20 |
|
|
Dynamic Fatigue Parameter(nd) |
- |
- |
≥ 20 |
|
Macro-bend Induced Attenuation |
|||
|
Ø60mm×100 |
1550nm |
dB |
≤ 0.05 |
|
1625nm |
dB |
≤ 0.05 |
|
|
*Higher screening tension products are available. |
|||