G.655 Non-zero dispersion shifted single-mode fiber
Product Performance
Meets the transmission requirements of C-band (1530nm-1565nm) and L-band (1565nm-1625nm) and multi-channel dense wavelength division multiplexing (DWDM) systems.
Low attenuation, dispersion, and zero dispersion slopes meet the requirements for high-speed transmission.
Accurate Mold Field Diameter (MFD) characteristics ensure low splice losses and good compatibility
Application Scenarios
The optical fiber of choice for long-distance, large-capacity dense wavelength division multiplexing (DWDM) optical fiber communication systems above 10Gbit/s.
Product Specification
|
Characteristics |
Conditions |
Units |
Specified values |
|
Optical Characteristics |
|||
|
Attenuation |
1550nm |
dB/km |
≤ 0.22 |
|
1625nm |
dB/km |
≤ 0.24 |
|
|
Relative wavelength attenuation changes |
1550nm VS. 1525-1575mn |
dB/km |
≤ 0.02 |
|
Zero Dispersion Wavelength(λ0) |
- |
nm |
≤ 1520 |
|
Zero Dispersion Slope |
- |
ps/nm2·km |
≤ 0.084 |
|
Dispersion in the wavelength range |
1530-1565nm |
ps/nm·km |
2.0-6.0 |
|
1565-1625nm |
ps/nm·km |
4.5-11.2 |
|
|
PMD |
- |
ps/√km |
≤ 0.2 |
|
Cable Cutoff Wavelength(λcc) |
- |
nm |
≤ 1450 |
|
Mode Field Diameter (MFD) |
1550mn |
μm |
9.6±0.5 |
|
Attenuation discontinuity |
1550mn |
dB |
≤ 0.05 |
|
Geometrical Characteristics |
|||
|
Cladding Diameter |
μm |
125±0.7 |
|
|
Cladding Non-Circularity |
% |
≤ 1.0 |
|
|
Core-Cladding Concentricity Error |
μm |
≤ 0.6 |
|
|
Coating Diameter |
μm |
242±7 |
|
|
Coating-Cladding Concentricity Error |
μm |
≤ 12 |
|
|
Curl (Radius) |
m |
≥ 4 |
|
|
Environmental Characteristics 1550nm &1625nm |
|||
|
Temperature Dependence Induced Attenuation |
-60℃ to +85℃ |
dB/km |
≤ 0.05 |
|
Damp Heat Dependence Induced Attenuation |
85℃ and 85% RH, for 30 days |
dB/km |
≤ 0.05 |
|
Watersoak Dependence Induced Attenuation |
23℃, for 30 days |
dB/km |
≤ 0.05 |
|
Dry Heat Induced Attenuation |
85℃, for 30 days |
dB/km |
≤ 0.05 |
|
Mechanical properties |
|||
|
Tension screening |
- |
GPa |
0.69 |
|
- |
kpsi |
100 |
|
|
Coating Strip Force |
peak force |
N |
1.3-8.9 |
|
typical average force |
N |
1.0-5.0 |
|
|
Tensile Strength |
Weber Probability 50% |
GPa |
≥ 4.00 |
|
Weber Probability 15% |
GPa |
≥ 3.20 |
|
|
Dynamic Fatigue Parameter(nd) |
- |
- |
≥ 20 |
|
Macro-bend Induced Attenuation |
|||
|
Ø30mm×100 |
1550nm |
dB |
≤ 0.05 |
|
1625nm |
dB |
≤ 0.05 |
|
|
Ø16mm×1 |
1550nm |
dB |
≤ 0.5 |
|
1625nm |
dB |
≤ 0.5 |
|