BoneCom® Conventional single-mode fiber G.652.D
Product Performance
Wider wavelength range for high-speed networks.
Accurate Mold Field Diameter (MFD) characteristics ensure low splice losses and good compatibility.
Application Scenarios
100G and B100G high-speed long-haul long-span backbones.
High-bandwidth metro networks and access networks.
Product Specification
|
Characteristics |
Conditions |
Units |
Specified values |
|
Optical Characteristics |
|||
|
Attenuation |
1310nm |
dB/km |
≤ 0.350 |
|
1383nm |
dB/km |
≤ 0.340 |
|
|
1550nm |
dB/km |
≤ 0.210 |
|
|
1625nm |
dB/km |
≤ 0.240 |
|
|
Relative wavelength attenuation changes |
1310nm VS. 1285-1330mn |
dB/km |
≤ 0.04 |
|
1550nm VS. 1525-1575mn |
dB/km |
≤ 0.03 |
|
|
Zero Dispersion Wavelength(λ0) |
- |
nm |
1300-1324 |
|
Zero Dispersion Slope |
- |
ps/nm2·km |
0.073-0.092 |
|
Dispersion |
1550nm |
ps/nm·km |
13.3-18.6 |
|
1625nm |
ps/nm·km |
17.2-23.7 |
|
|
PMD |
- |
ps/√km |
≤ 0.15 |
|
Cable Cutoff Wavelength(λcc) |
- |
nm |
≤ 1260 |
|
Mode Field Diameter (MFD) |
1310nm |
μm |
9.2±0.4 |
|
1550mn |
μm |
10.4±0.5 |
|
|
Attenuation Discontinuity |
1310nm |
dB |
≤ 0.03 |
|
1550mn |
dB |
≤ 0.05 |
|
|
Attenuation of the two-way end difference |
1310nm |
dB/km |
≤ 0.04 |
|
1550nm |
dB/km |
≤ 0.04 |
|
|
Geometrical Characteristics |
|||
|
Cladding Diameter |
μm |
125±0.7 |
|
|
Cladding Non-Circularity |
% |
≤ 1.0 |
|
|
Core-Cladding Concentricity Error |
μm |
≤ 0.6 |
|
|
Coating Diameter |
μm |
242±7 |
|
|
200±10 |
|||
|
Coating-Cladding Concentricity Error |
μm |
≤ 12 |
|
|
Curl (Radius) |
m |
≥ 4 |
|
|
Environmental Characteristics 1550nm &1625nm |
|||
|
Temperature Dependence Induced Attenuation |
-60℃ to +85℃ |
dB/km |
≤ 0.03 |
|
Damp Heat Dependence Induced Attenuation |
85℃ and 85% RH, for 30 days |
dB/km |
≤ 0.03 |
|
Watersoak Dependence Induced Attenuation |
23℃, for 30 days |
dB/km |
≤ 0.03 |
|
Dry Heat Induced Attenuation |
85℃, for 30 days |
dB/km |
≤ 0.03 |
|
Mechanical properties |
|||
|
Tension screening * |
- |
GPa |
0.69 |
|
- |
kpsi |
100 |
|
|
Coating Strip Force |
peak force |
N |
1.3-8.9 |
|
typical average force |
N |
1.0-5.0 |
|
|
Tensile Strength |
Weber Probability 50% |
GPa |
≥ 4.00 |
|
Weber Probability 15% |
GPa |
≥ 3.20 |
|
|
Dynamic Fatigue Parameter(nd) |
- |
- |
≥ 20 |
|
Macro-bend Induced Attenuation |
|||
|
Ø60mm×100 |
1550nm |
dB |
≤ 0.05 |
|
1625nm |
dB |
≤ 0.05 |
|
|
Ø20mm×1 |
1550nm |
dB |
≤ 0.05 |
|
1625nm |
dB |
≤ 0.05 |
|
|
*Higher screening tension products are available. |
|||
Partner
Hot Tags: g.652.d, China g.652.d manufacturers, suppliers, fiber optic cable for indoor systems, building vertical cable expansion fiber optic cables, optical cable for indoor communication, indoor optical fibre link cable, building vertical cable retrofit fiber optic cables, optical cables for vertical cable management in buildings