BoneCom® Low-loss single-mode fiber LL-G.652.D
Product Performance
Wavelength attenuation coefficients: 1550nm≤ 0.185 dB/km, 1310nm≤0.330 dB/km
Accurate Mold Field Diameter (MFD) characteristics ensure low splice losses and good compatibility.
Application Scenarios
100G and B100G high-speed long-haul long-span backbones.
400G ultra-high-speed network construction.
High-bandwidth metro network.
Product Specification
|
Characteristics |
Conditions |
Units |
Specified values |
|
Optical Characteristics |
|||
|
Attenuation |
1310nm |
dB/km |
≤ 0.330 |
|
1383nm |
dB/km |
≤ 0.330 |
|
|
1550nm |
dB/km |
≤ 0.185 |
|
|
1625nm |
dB/km |
≤ 0.220 |
|
|
Relative wavelength attenuation changes |
1310nm VS. 1285-1330mn |
dB/km |
≤ 0.04 |
|
1550nm VS. 1525-1575mn |
dB/km |
≤ 0.03 |
|
|
Zero Dispersion Wavelength(λ0) |
- |
nm |
1300-1324 |
|
Zero Dispersion Slope |
- |
ps/nm2·km |
0.073-0.092 |
|
Dispersion |
1550nm |
ps/nm·km |
13.3-18.6 |
|
1625nm |
ps/nm·km |
17.2-23.7 |
|
|
PMD |
- |
ps/√km |
≤ 0.1 |
|
Cable Cutoff Wavelength(λcc) |
- |
nm |
≤ 1260 |
|
Mode Field Diameter (MFD) |
1310nm |
μm |
9.2±0.4 |
|
1550mn |
μm |
10.4±0.5 |
|
|
Attenuation discontinuity |
1310nm |
dB |
≤ 0.03 |
|
1550mn |
dB |
≤ 0.03 |
|
|
Attenuation of the two-way end difference |
1310nm |
dB/km |
≤ 0.03 |
|
1550nm |
dB/km |
≤ 0.03 |
|
|
Geometrical Characteristics |
|||
|
Cladding Diameter |
μm |
125±0.7 |
|
|
Cladding Non-Circularity |
% |
≤ 1.0 |
|
|
Core-Cladding Concentricity Error |
μm |
≤ 0.6 |
|
|
Coating Diameter |
μm |
242±7 |
|
|
200±10 |
|||
|
Coating-Cladding Concentricity Error |
μm |
≤ 12 |
|
|
Curl (Radius) |
m |
≥ 4 |
|
|
Environmental Characteristics 1550nm &1625nm |
|||
|
Temperature Dependence Induced Attenuation |
-60℃ to +85℃ |
dB/km |
≤ 0.03 |
|
Damp Heat Dependence Induced Attenuation |
85℃ and 85% RH, for 30 days |
dB/km |
≤ 0.03 |
|
Watersoak Dependence Induced Attenuation |
23℃, for 30 days |
dB/km |
≤ 0.03 |
|
Dry Heat Induced Attenuation |
85℃, for 30 days |
dB/km |
≤ 0.03 |
|
Mechanical properties |
|||
|
Tension Screening * |
- |
GPa |
0.69 |
|
- |
kpsi |
100 |
|
|
Coating Strip Force ** |
peak force |
N |
1.3-8.9 |
|
typical average force |
N |
1.0-5.0 |
|
|
Tensile Strength |
Weber Probability 50% |
GPa |
≥ 4.00 |
|
Weber Probability 15% |
GPa |
≥ 3.20 |
|
|
Dynamic Fatigue Parameter(nd) |
- |
- |
≥ 20 |
|
Macro-bend Induced Attenuation |
|||
|
Ø60mm×100 |
1550nm |
dB |
≤ 0.05 |
|
1625nm |
dB |
≤ 0.05 |
|
|
*Higher screening tension products are available. **At a coating diameter of 200±10, the coating peel force peaks at 0.6-8.9 N and averages 0.6-5.0N. |
|||
Partner
Hot Tags: ll-g.652.d, China ll-g.652.d manufacturers, suppliers, building vertical networking fiber optic cables, optical cables for vertical cable integration in buildings, optical cables for vertical trunking in buildings, vertical wiring optical cables in buildings, optical fibre patch cable for indoor, optical cables for vertical cable connectivity in buildings